薄膜衬里农业应用食品包装LLDPE 泰国PTT化学 LL7410D 薄膜级
- 品牌：泰国PTT化学
- 货号：333
- 价格： ￥12/千克
- 发布日期： 2023-07-12
- 更新日期： 2024-10-23
产品详请
| 品牌 | 泰国PTT化学 |
| 货号 | 333 |
| 用途 | 薄膜衬里农业应用食品包装 |
| 特性级别 | 增强级|||热稳定性|||高滑动||| |
| 牌号 | LL7410D |
| 型号 | LL7410D |
| 加工级别 | 吹膜级||| |
| 品名 | LLDPE |
| 外形尺寸 | 25 |
| 用途级别 | 通用级|||薄膜级|||家电部件||| |
| 生产企业 | 泰国PTT化学 |
| 是否进口 | 是 |
InnoPlus LL7410D
Linear Low Density Polyethylene
PTT Global Chemical Public Company Limited
产品说明：
InnoPlus LL7410D resin is a linear low density polyethylene with butene comonomers, with high content of slip and antiblock. This grade offers the excellent machinability on conversion lines. Films extruded from InnoPlus LL7410D have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing.
InnoPlus LL7410D is recommended for producing general purpose films, liners, food packaging, heavy duty and agricultural films.
InnoPlus LL7410D is recommended for producing general purpose films, liners, food packaging, heavy duty and agricultural films.
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.921 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 模压成型) | 52 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 模压成型 | 11.0 | MPa | ASTM D638 |
| 断裂, 模压成型 | 28.0 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 790 | % | ASTM D638 |
| 弯曲模量 (模压成型) | 310 | MPa | ASTM D790 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 25 | μm | |
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD : 25 μm, 吹塑薄膜 | 190 | MPa | ASTM D882 |
| 1% 正割, TD : 25 μm, 吹塑薄膜 | 220 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 25 μm, 吹塑薄膜 | 34.0 | MPa | ASTM D882 |
| TD : 断裂, 25 μm, 吹塑薄膜 | 26.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 25 μm, 吹塑薄膜 | 700 | % | ASTM D882 |
| TD : 断裂, 25 μm, 吹塑薄膜 | 900 | % | ASTM D882 |
| 落锤冲击 (25 μm, 吹塑薄膜) | 90 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 25 μm, 吹塑薄膜 | 100 | g | ASTM D1922 |
| TD : 25 μm, 吹塑薄膜 | 350 | g | ASTM D1922 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 (模压成型) | 440 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 97.0 | °C | ASTM D1525 |
| 熔融峰值温度 | 121 | °C | ASTM D3418 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (45°, 25.0 μm, 吹塑薄膜) | 50 | ASTM D2457 | |
| 雾度 (25.0 μm, 吹塑薄膜) | 17 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | 160 到 180 | °C | |
| 口模温度 | 170 到 190 | °C |