Lotrène® LLDPE Q1018H
Linear Low Density Polyethylene
QATOFIN Company Limited
产品说明：
Lotrène® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer.
They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
Lotrène® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks,
refuse, tunnel films, mulching films…
They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
Lotrène® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks,
refuse, tunnel films, mulching films…
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.918 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD : 40 μm, 吹塑薄膜 | 215 | MPa | ASTM D882 |
| 1% 正割, TD : 40 μm, 吹塑薄膜 | 245 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 40 μm, 吹塑薄膜 | 11.0 | MPa | ASTM D882 |
| TD : 屈服, 40 μm, 吹塑薄膜 | 11.0 | MPa | ASTM D882 |
| MD : 断裂, 40 μm, 吹塑薄膜 | 38.0 | MPa | ASTM D882 |
| TD : 断裂, 40 μm, 吹塑薄膜 | 33.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 40 μm, 吹塑薄膜 | 800 | % | ASTM D882 |
| TD : 断裂, 40 μm, 吹塑薄膜 | 850 | % | ASTM D882 |
| 落锤冲击 1(40 μm, 吹塑薄膜) | 150 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 40 μm, 吹塑薄膜 | 280 | g | ASTM D1922 |
| TD : 40 μm, 吹塑薄膜 | 480 | g | ASTM D1922 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 100 | °C | ASTM D1525 |
| 结晶峰温度 (DSC) | 122 | °C | 内部方法 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (45°, 40.0 μm, 吹塑薄膜) | 60 | ASTM D2457 | |
| 雾度 (40.0 μm, 吹塑薄膜) | 11 | % | ASTM D1003 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒1区温度 | 180 到 220 | °C | |
| 料筒2区温度 | 180 到 220 | °C | |
| 料筒3区温度 | 180 到 220 | °C | |
| 料筒4区温度 | 180 到 220 | °C | |
| 料筒5区温度 | 180 到 220 | °C | |
| 熔体温度 | 200 | °C |
| 挤压说明 |
|---|
| Blow-up ratio: 2:1 to 3:1Die gap: >1.8 mm |