Ajedium™ Films -- Radel® R-5100 NT15
Polyphenylsulfone
Solvay Specialty Polymers
产品说明：
Radel® polyphenylsulfone is an amorphous thermoplastic material that offers exceptional hydrolytic stability, and toughness superior to other commercially available, high-temperature flims.
PPSU films have high deflection temperatures and outstanding resistance to environmental stress cracking. The polymer is inherently flame retardant. The excellent thermal stability makes films suitable for applications where very low shrink at high temperatures are needed. PPSU films also have good electrical properties.
Radel® film is off-white in color.
PPSU films have high deflection temperatures and outstanding resistance to environmental stress cracking. The polymer is inherently flame retardant. The excellent thermal stability makes films suitable for applications where very low shrink at high temperatures are needed. PPSU films also have good electrical properties.
Radel® film is off-white in color.
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.30 | g/cm3 | ASTM D792 |
| 吸水率 (24 hr) | 0.37 | % | ASTM D570 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 撕裂阻力 | 8.1 | cN | ASTM D1004 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗撕裂蔓延性 | 140 | gf | ASTM D1922 |
| 面积系数 | 149 | ft2/lb/mil | |
| 薄膜厚度 - 经测试 | |||
| -- | 25 | μm | |
| -- 1 | 50 | μm | |
| -- 2 | 130 | μm | |
| 割线模量 | ASTM D882 | ||
| MD | 1590 | MPa | ASTM D882 |
| TD | 1980 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服 | 68.0 | MPa | ASTM D882 |
| TD : 屈服 | 59.0 | MPa | ASTM D882 |
| MD : 断裂 | 92.0 | MPa | ASTM D882 |
| TD : 断裂 | 70.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 屈服 | 9.2 | % | ASTM D882 |
| TD : 屈服 | 6.8 | % | ASTM D882 |
| MD : 断裂 | 140 | % | ASTM D882 |
| TD : 断裂 | 100 | % | ASTM D882 |
| 落锤冲击 | 750 | g | ASTM D1709B |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (1.8 MPa, 未退火, 3.18 mm) | 207 | °C | ASTM D648 |
| 玻璃转化温度 | 220 | °C | ASTM E1356 |
| 线形热膨胀系数 - 流动 (3.18 mm) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 9.0E+15 | ohms·cm | ASTM D257 |
| 介电强度 (0.0250 mm) | 190 | kV/mm | ASTM D149 |
| 介电常数 | 3.45 | ASTM D150 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 极限氧指数 | 38 | % | ASTM D2863 |