玻璃纤维增强材料LCP 日本 E130i-BK210P 注塑级
- 品牌：LCP 日本
- 货号：E130i-BK210P
- 价格： ￥98/千克
- 发布日期： 2024-06-18
- 更新日期： 2025-10-26
产品详请
| 品牌 | LCP 日本 |
| 货号 | E130i-BK210P |
| 用途 | 玻璃纤维增强材料, 30% 填料按重量 |
| 牌号 | |
| 型号 | E130i-BK210P |
| 品名 | LCP |
| 外形尺寸 | 25 |
| 生产企业 | LCP 日本 |
| 是否进口 | 是 |
VECTRA® E130i
Liquid Crystal Polymer
Celanese Corporation
30% 玻璃纤维增强材料
产品说明：
High temperature capability, easiest flow. Suitable where very thin walls are required. Used for broad range of SMT applications, with minimal dimensional change. 30% glass filled.
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
FDA compliant
UL-Listing V-0 in natural and black at .2mm thickness per UL 94 flame testing.
Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 240°C at 0.75mm.
UL = Underwriters Laboratories (USA)
Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
FDA compliant
UL-Listing V-0 in natural and black at .2mm thickness per UL 94 flame testing.
Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 240°C at 0.75mm.
UL = Underwriters Laboratories (USA)
物性信息：
| 基本信息 | |
|---|---|
|
|
|
| 填料/增强材料 |
|
| 特性 |
|
| RoHS 合规性 |
|
| 多点数据 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.61 | g/cm3 | ISO 1183 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 0.40 | % | ISO 294-4 |
| 流动方向 | 0.10 | % | ISO 294-4 |
| 吸水率 (平衡, 23°C, 50% RH) | 0.030 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (M 计秤) | 71 | ISO 2039-2 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 15000 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (断裂) | 150 | MPa | ISO 527-2/1A/5 |
| 拉伸应变 (断裂) | 1.6 | % | ISO 527-2/1A/5 |
| 弯曲模量 (23°C) | 13500 | MPa | ISO 178 |
| 弯曲应力 (23°C) | 220 | MPa | ISO 178 |
| 压缩模量 | 14000 | MPa | ISO 604 |
| 压缩应力 (1% 应变) | 93.0 | MPa | ISO 604 |
| 断裂弯曲应变 | 2.2 | % | ISO 178 |