PA6 德国巴斯夫 8202C 注塑级
- 价格: ¥20/千克
- 发布日期: 2025-03-25
- 更新日期: 2025-03-25
产品详请
Ultramid® 8202C
Polyamide 6
BASF Corporation
产品说明:
Ultramid 8202C is a modified crystalline and low viscosity, PA6 injection molding homopolymer. It is also available in heat stabilized (Ultramid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and chemical resistance.
Applications
Ultramid 8202C is ideally suited for applications such as: furniture casters, gears, window hardware, and fittings, insulators, bushings, valves, relays, wiring devices, and other electrical components.
Applications
Ultramid 8202C is ideally suited for applications such as: furniture casters, gears, window hardware, and fittings, insulators, bushings, valves, relays, wiring devices, and other electrical components.
物性信息:
| |
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
多点数据 |
|
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
比重 | 1.13 | -- | g/cm3 | ASTM D792, ISO 1183 |
收缩率 - 流动 (3.18 mm) | 0.90 | -- | % | |
吸水率 | ||||
24 hr | 1.6 | -- | % | ASTM D570 |
23°C, 24 hr | 1.6 | -- | % | ISO 62 |
饱和 | 9.3 | -- | % | ASTM D570 |
饱和, 23°C | 9.3 | -- | % | ISO 62 |
平衡, 50% RH | 2.6 | -- | % | ASTM D570 |
平衡, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
洛氏硬度 (R 级) | 120 | -- | ASTM D785 |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
拉伸模量 | ISO 527-2 | |||
-40°C | 4090 | -- | MPa | ISO 527-2 |
23°C | 3700 | 1360 | MPa | ISO 527-2 |
80°C | 750 | -- | MPa | ISO 527-2 |
120°C | 550 | -- | MPa | ISO 527-2 |
150°C | 445 | -- | MPa | ISO 527-2 |
抗张强度 | ||||
屈服, -40°C | 137 | 142 | MPa | ASTM D638, ISO 527-2 |
屈服, 23°C | 90.0 | 48.0 | MPa | ASTM D638 |
屈服, 80°C | 40.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
屈服, 121°C | 30.0 | 25.0 | MPa | ASTM D638 |
屈服, 23°C | 88.0 | 43.0 | MPa | ISO 527-2 |
屈服, 120°C | 30.0 | 25.0 | MPa | ISO 527-2 |
屈服, 150°C | 25.0 | -- | MPa | ISO 527-2 |
断裂, -40°C | 130 | 80.0 | MPa | ASTM D638 |
断裂, 23°C | 90.0 | 70.0 | MPa | ASTM D638 |
断裂, 80°C | 35.0 | 30.0 | MPa | ASTM D638 |
断裂, 121°C | 25.0 | 20.0 | MPa | ASTM D638 |