VESTAMID® L L-GF15

Polyamide 12

Evonik Industries AG

15% 玻璃纤维增强材料

产品说明：

Reinforced, filled and flame retardant polyamide 12 compounds
Characterization: 15% chopped strands, medium viscosity, heat stabilized, with processing aid
Application Examples: gear box housing for electrical car window lifts
The properties of PA 12 compounds can be modified to suit the requirements of many applications by incorporating various additives such as stabilizers, plasticizers, reinforcements, and fillers.
The VESTAMID® L compounds of Evonik comprise a range of various products that are customized to the requirements of processors and users. Many of the PA 12 compounds are suitable especially for the injection molding of recision parts; others have been developed specifically for the extrusion process.

物性信息：

基本信息

填料/增强材料	玻璃纤维增强材料, 15% 填料按重量
添加剂	加工助剂热稳定剂
特性	高 ESCR（抗应力开裂）减震降噪抗溶剂性抗撞击性，良好可加工性，良好良好耐磨损性耐疲劳性能耐燃油性耐油性能耐油脂性能热稳定性食品接触的合规性吸水低或不吸水中等粘性阻燃性
用途	汽车电子外壳
机构评级	欧洲 10/1/2011 12:00:00 AM
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度 (23°C)	1.12	g/cm3	ISO 1183
收缩率			ISO 294-4
垂直流动方向	0.65	%	ISO 294-4
流动方向	0.35	%	ISO 294-4
吸水率			ISO 62
饱和, 23°C	1.3	%	ISO 62
平衡, 23°C, 50% RH	0.60	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	3900	MPa	ISO 527-2
拉伸应力 (断裂)	95.0	MPa	ISO 527-2
拉伸应变 (断裂)	6.0	%	ISO 527-2

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度			ISO 179/1eA
-30°C, 完全断裂	11	kJ/m2	ISO 179/1eA
23°C, 完全断裂	17	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度			ISO 179/1eU
-30°C, 完全断裂	80	kJ/m2	ISO 179/1eU
23°C, 完全断裂	75	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa, 未退火	175	°C	ISO 75-2/B
1.8 MPa, 未退火	160	°C	ISO 75-2/A
维卡软化温度
--	175	°C	ISO 306/A
--	170	°C	ISO 306/B
熔融温度 1	178	°C	ISO 11357-3
线形热膨胀系数 - 流动 (23 到 55°C)	8.0E-5	cm/cm/°C	ISO 11359-2