Borealis PP BD310MO
Polypropylene Copolymer
Borealis AG
产品说明：
BD310MO is a heterophasic copolymer. This grade is characterized by an optimum combination of good impact strength and very high stiffness.
This grade is mildly nucleated to maximize the mechanical stiffness. This grade contains antistatic and demoulding additives which, together with enhanced nucleation, create a high potential for cycle time reduction.
This grade is mildly nucleated to maximize the mechanical stiffness. This grade contains antistatic and demoulding additives which, together with enhanced nucleation, create a high potential for cycle time reduction.
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.905 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| 收缩率 | 1.0 到 2.0 | % | ISO 294-4 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 计秤) | 91 | ISO 2039-2 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 (注塑) | 1400 | MPa | ISO 527-2/1 |
| 拉伸应力 (屈服, 注塑) | 28.0 | MPa | ISO 527-2/50 |
| 拉伸应变 (屈服, 注塑) | 6.0 | % | ISO 527-2/50 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -20°C | 4.5 | kJ/m2 | ISO 179/1eA |
| 23°C | 9.0 | kJ/m2 | ISO 179/1eA |
| 多轴向仪器化冲击能量 | ISO 6603-2 | ||
| -20°C | 10.0 | J | ISO 6603-2 |
| 0°C | 13.0 | J | ISO 6603-2 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (0.45 MPa, 未退火) | 92.0 | °C | ISO 75-2/B |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 230 到 260 | °C | |
| 模具温度 | 10.0 到 30.0 | °C | |
| 注射速度 | 快速 | ||
| 保压 | 20.0 到 50.0 | MPa |